Brass Rods
Your source for Brass Rods, Manufacturer and Supplier of the most qualitative range of Brass Rods
Look for Brass Rods at best price across industry.
Grand Metal Corporation is acknowledged as a manufacturer, exporter & suppliers of Brass Rods, available in a variety or grades, materials, and finishes, in metric and inch sizes. We have a full range available always, with unrivalled lead times, superior quality and exemplary customer service, leading Brass Rods.
Manufacturer & suppliers of manufacturers of forged brass rods, we aim to provide rods that meets all international standards and standardized finishes to meet the demands of industries including Electronics, Automobiles, Engineering, Electrical, Sanitary fittings, Building Hardware and others.
Useful Information of Brass Rods
Specification & Types of Brass Road:
Forging Brass Rods
• ASTM B 124 C37700
• BS 2874 CZ 122
• IS 3488 Forging Brass
Chemical Composition
| Chemical Requirements |
CuZn42Pb2 |
CuZn40Pb2 |
| Copper |
56.5 - 60.0% |
57.0 - 59.0% |
| Lead |
0.60 to 2.0% |
1.5 to 2.5% |
| Iron |
0.30% max |
0.40% max |
| Total Imp. Excl. Iron |
0.20% max |
0.70% max |
| Zinc |
Remainder |
Remainder |
| |
|
|
| ensile Strength |
380 Mpa Min |
40 kg/mm2 Min. |
| Elongation % |
25% Min |
18% Min. |
| Izod Value |
- |
2.0 KJ min |
Physical Property
| Capacity for being |
|
|
| Cold worked |
Poor |
Poor |
| Hot formed |
Excellent |
Excellent |
| Hot forgeability rating |
100% |
100% |
| Machinability Rating |
80% |
80% |
| Suitability for soldering |
Excellent |
Excellent |
| Suitability for Brazing |
Good |
Good |
High Tensile Brass Rods
• IS 320 HT1 or HT2
• BS 2874 CZ114 or CZ115
• JIS 3250H C6782 or C6783
Chemical Composition
| Chemical Requirements |
HT1 |
HT2 |
| Copper |
56.0 - 60.0% |
56.0 - 61.0% |
| Lead |
0.20 to 1.50% |
0.50 to 1.50% |
| Iron |
0.20 to 1.25% |
0.20 to 1.50% |
| Tin |
0.20 to 1.0% |
1.0% max |
| Aluminium |
0.2% max |
0.30 to 2% |
| Manganese |
0.25 - 2.0% |
0.50-2.0% |
| Total Imp. |
0.50% max |
0.50% max |
Physical Properties
| Condition |
Size |
T.S. MPa |
EL% Min |
T.S. MPa |
EL% Min |
| As manufactured |
All Size |
430 min |
20% |
460 min |
20% |
| Cold-worked & Stress |
Oct-40 |
480 min |
12% |
520 min |
12% |
| Relieved |
40 above |
|
|
500 min |
15% |
Fabrication Properties
| Capacity for being |
|
|
| Cold formed |
Poor |
Fair |
| Hot worked |
Good |
Good |
| Machinability Rating |
30% |
30% |
| Resistance to Corrosion |
Excellent |
Excellent |
| Suitability for soldering |
Excellent |
Fair |
Riveting Brass Rods
• IS 4170 CuZn40
• BS 2874 CZ109
• JIS 3250 H C2800
• ASTM B171 C 36500
• IS 4413 CuZn37
• BS 2872 CZ108
Chemical Composition
| Chemical Requirements |
CuZn35Pb1 |
CuZn35 |
| Copper |
62.0 - 65.0% |
63.0 - 68.0% |
| Lead |
0.75 to 1.50% |
0.02% max. |
| Iron |
0.10% max |
0.05% max |
| Total Imp. |
0.50% max |
0.30% max |
| Zinc |
Remainder |
Remainder |
Physical Properties
| Condition |
T.S. MPa |
EL% Min |
T.S. MPa |
EL% Min |
| Quarter Hard (HA) |
325-390 |
30% |
340-345 |
30% |
| Half-Hard (HB) |
400-490 |
20% |
420-510 |
15% |
| Hard (HD) |
500-685 |
15% |
- |
- |
| Extra Hard (HE) |
695-885 |
5% |
- |
- |
Fabrication Properties
| Capacity for being |
|
| Cold forming |
Excellent |
| Machinability Rating |
70% |
| Bending |
Excellent |
| Riveting |
Excellent |
Contact Grand Metal Corporation today for a best offer & competitive quotation…